Sonochemical synthesis of latex
Hielscher Ultrasonicscontact supplier
Hielscher Ultrasonics describes how ultrasound promotes the chemical reaction for the polymerisation of latex.
Latex particles are widely used as additive for various materials. Common application fields include the use as additives in paints and coatings, glues and cement.
The high potential of ultrasonics is the capability of creating dispersions and emulsions not only in the micron- but also in the nano-size range. For the synthesis of latex, an emulsion or dispersion of monomers, e.g. polystyrene, in water (o/w = oil-in-water emulsion) is the basis of the reaction.
Depending on the emulsion type, a small amount of surfactant may be required, but often the ultrasonic energy provides such a fine droplet distribution so that the surfactant is superfluous.
If ultrasound with high amplitudes is introduced into liquids, the phenomenon of so-called cavitation occurs.
The liquid bursts and vacuum bubbles are generated during the alternating high-pressure and low-pressure cycles. When these small bubbles cannot absorb more energy, they implode during a high-pressure cycle, so that pressures up to 1000 bar and shock waves as well as liquid jets of up to 400 km/h are reached locally.
These highly intense forces, caused by ultrasonic cavitation, take effect to the enclosing droplets and particles.
The free radicals formed under the ultrasonic cavitation initiate the chain reaction polymerisation of the monomers in the water. The polymer chains grow and form primary particles with an approximate size of 10-20 nm.
The primary particles swell with monomers, and the initiation of polymer chains continues in the aqueous phase, growing polymer radicals are trapped by the existing particles, and polymerisation continues inside the particles.
After the primary particles have formed, all further polymerisation increases the size but not the number of particles. Growth continues until all of the monomer is consumed. The final particle diameters typically are 50-500 nm.
If polystyrene latex is synthesised via sonochemical route, latex particles with a small size of 50 nm and a high molecular weight of more than 106 g/mol can be achieved.
Due to the efficient ultrasonic emulsification, only a small amount of surfactant will be needed. The continuous ultrasonication applied to the monomer solution creates sufficient radicals around the monomer droplets, which leads to the very small latex particles during the polymerisation.
Besides the ultrasonic polymerisation effects, further benefits of this method are the low reaction temperature, the faster reaction sequence and the quality of the latex particles due to the high molecular weight of the particles. The advantages of ultrasonic polymerisation apply also for the ultrasonically-assisted copolymerisation.
A potential effect of latex is achieved by the synthesis of ZnO encapsulated nanolatex: The ZnO encapsulated nanolatex shows high anticorrosive performance.
In the study of Sonawane et al. (2010), ZnO/poly(butyl methacrylate and ZnO−PBMA/polyaniline nanolatex composite particles of 50 nm have been synthesised by sonochemical emulsion polymerisation.
Hielscher Ultrasonics high-power devices are reliable and efficient tools for sonochemical reaction. A wide range of ultrasonic processors with different power capacities and setups makes sure to provide the optimal configuration for the specific process and volume.
All applications can be evaluated in the lab and subsequently scaled up to the production size, linearly. Ultrasonic machinery for continuous processing in the flow-through mode can be easily retrofitted into existing production lines.
Hielscher has summarised the features of its most innovative ultrasonic devices for liquid processing.
Hielscher describes how ultrasound can offer a better alternative to removing sulphur from crude oil and petroleum products.
Hielscher describes the ultrasonic extraction of coffee compounds and how this could be beneficial to a wide range of industries.
Hielscher describes the ultrasonic dispersing, synthesis and funtionilisation of nanodiamonds.
Hielscher takes an in-depth look at ultrasonic preparation of graphene and its potential applications.